Phase-shifting photomask blank, phase-shifting photomask, method for producing them and apparatus for manufacturing the blank

ABSTRACT

A uniform thin phase-shifting photomask blank can be formed by depositing a thin film on a substrate by a reactive sputtering technique while passing, at least four times, the substrate over a sputtering target. In the formation of the blank, NO gas is used as the reactive gas, a target composed of a mixture of molybdenum and silicon is used as the sputtering target and a transparent substrate is used as the thin film-forming substrate to form, on the transparent substrate, a light-transmitting film capable of transmitting light rays having an intensity, which cannot substantially contribute to the exposure. In addition, the film is formed, on the substrate, through an opening having a sufficiently enlarged length along the substrate-conveying direction so that even regions whose deposition rate of the target component is not more than 90% of the maximum level thereof also contribute to the film-formation. The phase-shifting photomask blank thus prepared is subjected to a patterning treatment to form a phase-shifting photomask.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to a method for preparing a thin film and more particularly to a phase-shifting photomask blank which permits the improvement of transferred patterns in their resolution by making a difference in phase between exposed light rays passing through a mask and a phase-shifting photomask prepared from the phase-shifting photomask blank as well as a method for producing the photomask blank and the photomask and an apparatus for manufacturing the phase-shifting photomask blank. In other words, the present invention relates to a so-called half-tone type phase-shifting photomask blank, a phase-shifting photomask as well as a method for producing them and an apparatus for manufacturing the phase-shifting photomask blank.

[0003] 2. Disclosure of the Related Art

[0004] In case of a phase-shifting photomask 208 as shown in FIG. 21(B), a circuit pattern 230 to be transferred onto a semiconductor substrate has in general been formed by making use of a phase-shifting photomask which is produced by etching the surface of a phase-shifting photomask blank 200 which consists of a quartz substrate 201 and a phase-shifting film 204, as shown in FIG. 21(A), to remove a desired portion of the film 204 and to thus form openings 210 through which the surface of the quartz substrate 201 is exposed and phase-shifting portions 205, i.e., the unetched portions of the film 204 remaining on the substrate.

[0005] The phase-shifting portion 205 has light-transmission properties to the exposed light rays and the thickness thereof is designed in such a manner that a phase of the exposed light rays transmitting through the opening 210 has a phase difference, by 180 degrees, from that of the light rays transmitting through the phase-shifting portion 205. Therefore, when exposing a wafer as shown in FIG. 21(C) to light rays, the light intensity observed on the wafer at the boundary between the opening 210 and the phase-shifting portion 205 becomes zero. For this reason, the circuit pattern transferred using the phase-shifting photomask 208 would have a high resolution.

[0006] As the phase-shifting film 204, there have in general been used a monolayer or multi-layer film and it has been desired for the phase-shifting portion 205 to have a light-transmittance to the exposed light rays in the range of from 4% to 40% in order to obtain an appropriate quantity of exposed light rays during lithography operations and to control the thickness, as determined after development, of a resist film applied onto the wafer.

[0007] Up to now, when forming a monolayer phase-shifting film 204 having a desired thickness on a substrate on which a film is deposited (hereinafter simply referred to as “film-forming substrate”) in order to form a phase-shifting photomask blank as shown in FIG. 21(A) using a film-forming device wherein a reactive gas is supplied to a film-forming chamber and a thin film is formed on the film-forming substrate according to the reactive sputtering technique while passing the substrate over a sputtering target, a film is formed by passing the substrate over the target only one time by controlling the deposition rate of the film on the substrate and the conveying speed of the substrate in such a manner that a desired film thickness can be obtained by a single pass (see, for instance, Japanese Un-Examined Patent Publication (hereinafter referred to as “J.P. KOKAI”) No. Hei 9-17928). The disclosure of the above publication is hereby incorporated by reference herein.

[0008] Such a conventional technique will hereinafter be described with reference to the attached FIG. 1. FIG. 1 shows a part of a film-forming chamber 11 of a film-forming device. A mixed gas comprising a sputtering gas and a reactive gas is supplied to the film-forming chamber through a gas-supply port 14 after vacuum exhaustion through an exhaust port 15. A DC voltage which is negative with respect to the grounding voltage is applied to a sputtering target 12 (MoSi) to thus form a discharge zone in the proximity to the sputtering target and as a result, the target 12 begins to discharge sputter materials. If a film-forming quartz substrate 101 is continuously conveyed along a conveying path 18 positioned at a predetermined distance from the target 12, a desired film is formed on the substrate.

[0009] As has been discussed above, when forming the monolayer film having a desired thickness on the film-forming substrate using the film-forming device wherein the reactive gas is supplied to the film-forming chamber and the film is formed on the film-forming substrate according to the reactive sputtering technique while passing the substrate over the sputtering target, the thin film has conventionally been formed by passing the substrate over the target only one time by controlling the deposition rate of the film on the substrate and the conveying speed of the substrate in such a manner that a desired film thickness can be obtained by a single pass. In this case, however, the thickness distribution of the monolayer film has a tendency as shown in FIG. 1. More specifically, FIG. 1 shows the deposition rate distribution of the target component 19-1 (or the thickness distribution of the target component formed on a static substrate). The distribution of the target component along a conveying path 18 is not uniform and therefore, the higher the deposition rate of the target component along the conveying path 18, the larger the amount of the unreacted target component if it is assumed that the frequency of the reactive gas incident upon the substrate 101 is approximately constant along the conveying path 18 as shown in FIG. 1 (see line 19-2). Accordingly, the content of the reaction product in the resulting film is low and a non-uniform film is formed on the conveyed substrate. If an opening 17-1 positioned between shielding plates 17 is divided into regions A, B and C arranged along the conveying path 18, a non-uniform film 31 shown in FIG. 2 is formed on the substrate 101 by a single forward movement of the substrate 101, in a horizontal direction, over a target 12. The non-uniform film is thus formed on the substrate and this accordingly results in various drawbacks. For instance, the resulting film shows optical characteristics which are widely different from those expected for a uniform monolayer film and exhibits resistance to chemicals considerably inferior to that of a uniform film. Moreover, this film cannot optically be handled as a monolayer film and this in turn results in such disadvantages that this makes the calculation of the optical constants quite difficult and that the design and the quality control of films become difficult. In order to eliminate such drawbacks, it has been devised to reduce the lengths of the opening 17-1 of the shielding plate and that of a chimney 13 along the substrate-conveying direction (this is referred to as “opening length”) so that only the region B (for instance, the region whose deposition rate is not less than 90% of the maximum level thereof) in which the deposition rate of the target component is approximately constant contributes to the film-formation, or so that even a part of the region A contributes to the film-formation. However, the former suffers from a problem of reduction of the utilization efficiency of the target 12 (the ratio of the amount of the target capable of being used in the film-formation to the total consumed amount thereof) and productivity, while the latter suffers from a problem of, for instance, the reduction in the utilization efficiency of the target according to the reduction in the opening length, the deterioration of the resistance to chemicals due to the non-uniformity of the film composition and complication of optical characteristics.

SUMMARY OF THE INVENTION

[0010] Accordingly, it is generally an object of the present invention to solve the foregoing problems associated with the conventional sputtering techniques and specifically to provide a substantially uniform thin film which can ensure optical characteristics quite similar to those expected for a uniform monolayer film and resistance to chemicals almost comparable to is that observed for a uniform monolayer film without impairing the utilization efficiency of a target and productivity of films and which can optically be handled as a substantial monolayer film and which makes the calculation of optical constants of the film, the design and the quality control thereof easy, in particular, a phase-shifting photomask blank and a phase-shifting photomask excellent in resistance to chemicals and optical characteristics.

[0011] Another object of the present invention is to provide a phase-shifting photomask which can be prepared from the foregoing phase-shifting photomask blank.

[0012] A further object of the present invention is to provide a method for preparing such a phase-shifting photomask blank and such a phase-shifting photomask.

[0013] Still another object of the present invention is to provide a device for manufacturing such a phase-shifting photomask blank.

[0014] According to a first aspect of the present invention, there is provided a method for preparing a thin film which comprises supplying a reactive gas to a film-forming chamber and depositing a film on a film-forming substrate by the reactive sputtering technique while passing the substrate over a sputtering target, wherein the film is formed while passing, at least 4 times, the substrate over the target and establishing sufficient lengths of the openings of shielding plate and chimney to thus form a substantially uniform film on the substrate without impairing the utilization efficiency of the target and the productivity of the film. The method makes it easy to produce, in particular, a desired phase-shifting photomask blank and a desired phase-shifting photomask.

[0015] According to a second aspect of the present invention, there is provided a phase-shifting photomask blank which comprises a thin film formed on a substrate according to the reactive sputtering technique in which a reactive gas is supplied to a film-forming chamber and a film is formed on a film-forming substrate while passing, at least 4 times, the substrate over a sputtering target.

[0016] According to a third aspect of the present invention, there is provided a phase-shifting photomask which comprises a pattern consisting of light semitransparent portions and light transmitting portions transparent to light rays having an intensity substantially contributing to light-exposure, the pattern being produced by subjecting the light semitransparent film of the foregoing phase-shifting photomask blank to a pattern-forming or patterning treatment to thus remove a part of the light semitransparent film.

[0017] According to a fourth aspect of the present invention, there is provided a device for manufacturing a phase-shifting photomask blank in which a film is formed by supplying a reactive gas to a film-forming chamber and depositing a thin film on a film-forming substrate using the reactive sputtering technique, while passing the substrate over a sputtering target, and which is designed so that even regions whose deposition rate of the target component is not more than 90% of the maximum level thereof also contribute to the film-formation by sufficiently enlarging an opening length along the substrate-conveying direction.

BRIEF DESCRIPTION OF THE DRAWINGS

[0018] The aforementioned and other objects, features and advantages of the present invention will become more apparent from the following description taken with reference to the accompanying drawings, wherein:

[0019]FIG. 1 is a schematic partial diagrammatic view for explaining the film-forming chamber of a film-forming device used in the present invention;

[0020] FIGS. 2 to 5 are diagrams for explaining various film-forming processes used in Examples of the present invention;

[0021]FIG. 6 is a graph showing the relation between the phase difference and the number of film-forming steps observed for the thin film prepared in Example 1;

[0022]FIG. 7 is a graph showing the relation between the resistance to an aqueous ammonia solution and the number of film-forming steps observed for the thin film prepared in Example 1 as expressed in terms of the film thickness, film surface reflectivity, transmittance and rate of variation of phase difference;

[0023]FIG. 8 is a diagram showing the results obtained by analyzing the film composition of the sample No. 1 prepared in Example 1, using an Auger electron spectrometer;

[0024]FIG. 9 is a diagram showing the results obtained by analyzing the film composition of the sample No. 2 prepared in Example 1, using an Auger electron spectrometer;

[0025]FIG. 10 is a diagram showing the results obtained by analyzing the film composition of the sample No. 4 prepared in Example 1, using an Auger electron spectrometer;

[0026]FIG. 11 is a diagram showing the results obtained by analyzing the film composition of a uniform film sample No. 26 (reference sample) given in Example 7 for the purpose of comparison, using an Auger electron spectrometer;

[0027]FIG. 12 is a graph showing the relation between the phase difference and the number of film-forming steps observed for the thin film prepared in Example 1;

[0028]FIG. 13 is a graph showing the relation between the refractive index and the number of film-forming steps observed for the thin film prepared in Example 1;

[0029]FIG. 14 is a graph showing the relation between the extinction coefficient and the number of film-forming steps observed for the thin film prepared in Example 1;

[0030]FIG. 15 is a graph showing the relation between the phase difference and the number of film-forming steps observed for the thin film prepared in Example 2;

[0031]FIG. 16 is a graph showing the relation between the resistance to an aqueous ammonia solution and the number of film-forming steps observed for the film of Sample Nos. 21 to 25 prepared in Example 2 as expressed in terms of the film surface reflectivity, transmittance and rate of variation of phase difference;

[0032]FIG. 17 is a graph showing the relation between the resistance to an aqueous ammonia solution and the number of film-forming steps observed for the film of Sample Nos. 31 to 35 prepared in Example 2 as expressed in terms of the film surface reflectivity, transmittance and rate of variation of phase difference;

[0033]FIG. 18 shows schematic diagrams for explaining the film-forming steps performed in Example 5, in which (A) is a cross-sectional view of a molybdenum silicide oxynitride (MoSiON) film produced in Example 5 according to the present invention; and (B) to (E) are diagrams each for explaining a part of the steps in Example 5;

[0034]FIG. 19 is a cross-sectional view of a quasi-bilayer film of molybdenum silicide oxynitride (MoSiON) produced in Example 6 according to the present invention;

[0035]FIG. 20 is a diagram for explaining a part of the steps performed in Example 6 according to the present invention;

[0036] FIGS. 21(A) to (C) are a cross-sectional view of a phase-shifting photomask blank, a cross-sectional view of a phase-shifting photomask, and a diagram for explaining the intensity of the exposed light rays observed on the surface of a wafer;

[0037] FIGS. 22(A) to (D) each is a diagram for explaining a part of the steps performed in Example 7 according to the present invention;

[0038] FIGS. 23(A) to (E) each is a diagram for explaining a part of the steps performed in Example 8 according to the present invention; and

[0039] FIGS. 24(A) and (B) each is a diagram for explaining a part of the steps performed in Example 9 according to the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0040] In the present invention, a film is formed by passing, at least 4 times, a film-forming substrate over a target. Therefore, the resulting film has a periodic structure consisting of at least 4 non-uniform unitary films each of which is formed on the substrate by a single film-forming step, the distribution of compositions along the thickness of the thin films formed is thus substantially equalized and the resulting film would exhibit the resistance to chemicals and optical characteristics substantially identical to those observed for a uniform film.

[0041] The method for preparing a phase-shifting photomask blank according to the present invention preferably utilizes NO gas as the reactive gas, a target composed of a mixture of molybdenum and silicon as the sputtering target and a transparent substrate as the thin film-forming substrate to thus form a light-transmitting film capable of transmitting light rays having an intensity, which cannot substantially contribute to the exposure, on the transparent substrate.

[0042] Moreover, in the foregoing method, it is desirable that the method be designed in such a manner that even the regions whose deposition rate of the target component is not more than 90% of the maximum level thereof also contribute to the film-formation by forming a film through an opening having a sufficiently enlarged length along the substrate-conveying direction.

[0043] According to the present invention, a phase-shifting photomask can be prepared by producing a phase-shifting photomask blank by the foregoing production method, removing a part of the light translucent film of the blank by subjecting it to a patterning treatment to thus form a pattern consisting of the resulting light translucent portions and light-transmitting portions capable of transmitting light having an intensity which can substantially contribute to the exposure.

[0044] In the present invention, the patterning of the foregoing phase-shifting photomask blank can be performed by any light-exposure process such as light rays- or electron beam-exposure techniques. When carrying out this electron beam exposure, it is desirable that a metallic antistatic film be deposited directly on a shifter film formed on the substrate and then a resist for electron beam exposure be applied thereon prior to the electron beam exposure or that a resist for electron beam exposure be formed on a phase-shifter film (or a metallic antistatic film is applied onto the phase-shifter film and then a resist for electron beam exposure be applied thereon) and then a non-metallic antistatic film be formed thereon. This is because if a film free of any electrical conductivity such as a molybdenum silicide oxynitride film is used as the phase-shifter film and the phase-shifter film is subjected to the electron beam exposure without any pre-treatment, the phase-shifter film would cause static electrification and accordingly, such an antistatic film is applied in advance. As such antistatic films, there may be used, for instance, non-metallic antistatic films such as Espacer 100 and 300 (registered trade marks in Japan) available from Showa Denko K.K. and aqua SAVE-53za available from Nitto Chemical Industry Co., Ltd.; and metallic antistatic films such as those comprising Mo, Cr, W, Ta, Ti, Si, Al or the like, or alloys thereof.

[0045] In addition, the device for manufacturing the phase-shifting photomask blank according to the present invention has been developed for practicing the foregoing method of the present invention and in particular, the device is designed in such a manner that even the regions whose deposition rate of the target component is not more than 90% of the maximum level thereof also contribute to the film-formation by sufficiently enlarging the length of the opening along the substrate-conveying direction.

[0046] The present invention will hereinafter be described in more detail with reference to Examples and Comparative Examples as well as the accompanying drawings. These Examples are given only for the illustration of the present invention and are not to be construed as limiting the scope of the present invention.

[0047] First of all, the present invention will be described in detail with reference to FIGS. 1 to 5 attached hereto. FIG. 1 shows a part of the film-forming chamber 11 of a film-forming device. This device comprises two cathodes having the same structure and positioned in proximity to one another and either of them can be used, but only one 32 of these depicted cathodes is used in the following description for the sake of simplicity, unless otherwise specified. After exhausting the film-forming chamber 11 to a vacuum, a gas mixture of a sputtering gas and a reactive gas is supplied to the chamber through a gas supply port 14. A DC voltage which is negative relative to the grounding voltage is applied to a sputtering target 12 (MoSi). Thus, a discharge zone is established in the proximity to the sputtering target and as a result, a target material is discharged from the sputtering target 12. When film-forming quartz substrates 101 are continuously conveyed in the chamber along a conveying path 18 positioned at a predetermined distance from the sputtering target 12, a unitary film (a film formed by a single pass) is formed on the substrate every passage of the substrate through an opening 17-1 of a shielding plate 17. In FIG. 1, the length of the opening 17-1 is adjusted to one approximately identical to that of an opening of a chimney 13, but the latter may be shorter than the former. In any case, it is sufficient that these openings are designed in such a manner that even the regions whose deposition rate of the target material is not more than 90% of the maximum level thereof can also contribute to the film-formation by sufficiently enlarging the length of the opening along the substrate-conveying direction. In FIG. 1, the reference numeral 16 means grounding shield.

[0048] As will be clear from the distribution 19-1 of the target component-deposition rate (or the thickness distribution of the target component in the film formed on a substrate at rest) as shown in FIG. 1, the target component is non-uniformly distributed along the conveying path 18. Therefore, if it is assumed that the frequency of the reactive gas incident upon the substrate 101 is approximately constant along the conveying path 18 as shown by a curve 19-2, the higher the target component-deposition rate along the conveying path 18, the greater the amount of the unreacted target component and thus the content of the reaction product in the resulting film is reduced and this leads to the formation of a non-uniform film on the conveyed substrate.

[0049] If the opening 17-1 of the shielding plate 17 is divided into three zones A, B and C along the conveying path 18, a non-uniform film denoted by the reference numeral 31 in FIG. 2 is formed on the substrate 101 by a single forward movement of the substrate 101 in a horizontal direction. Similarly, a non-uniform film denoted by the reference numeral 41 in FIG. 3 is formed on the substrate 101 by a single backward movement of the substrate 101 in the horizontal direction.

[0050] A film having a periodic structure (comprising film-constituting elements 51 to 54) as shown in FIG. 4 is formed by repeating the forward movement 4 times, i.e. by moving the substrate forth for 4 times, while if a film is formed by alternatively repeating the forward movement and backward movement 4 times in all, i.e. by moving the substrate back and forth for 2 times (one forward and backward movement cycle is repeated 2 times), a film having a periodic structure (comprising film-constituting elements 81 to 84) as shown in FIG. 5 is obtained.

[0051] The present invention will be detailed below with reference to the following Examples, but the present invention is not restricted to these specific Examples at all and it is possible to envisage other variations thereon without departing from the scope of the invention.

EXAMPLE 1

[0052] Table 1 shows conditions for manufacturing a variety of samples which are films each having a periodic structure formed by the forward movement or the forward or backward movements according to the foregoing procedures. Sample No. 1 is a film formed by a single forward movement of the substrate and Sample Nos. 2, 3, 4 and 5 are films formed by repeating the forward and backward movements 2, 3, 4 and 6 times, respectively. Sample No. 2 corresponds to the film having a layer structure as shown in FIG. 5 and comprises a non-uniform film, whose film-constituting elements are represented by the reference numerals 81 to 84, formed on the substrate 101.

[0053] Table 2 shows the results obtained by inspecting each sample listed in Table 1 for film thickness, i-line phase difference, spectral reflectance and spectral transmittance.

[0054] Table 3 shows i-line optical constants (refractive index (n) and extinction coefficient (k)) determined by the so-called RT method based on the measured results listed in Table 2 together with the phase difference calculated from the optical constants thus obtained and the film thickness for the purpose of comparison with the practically measured values.

[0055]FIG. 6 is a graph showing the measured phase difference values while comparing them with those calculated from the optical constants and the film thickness as shown in Table 3. In FIG. 6, the phase difference (deg.) is plotted as ordinate and the number of film-forming steps as abscissa.

[0056]FIG. 7 is a graph showing the results obtained in the 90 minute-immersion test wherein the samples listed in Table 1 and Sample No. 26 (reference example) listed in Table 7 were immersed in a 0.5% aqueous ammonia for 90 minutes.

[0057] In FIG. 7, the rates of change (%) in the transmittance, phase difference, film thickness and reflectance observed when light rays are incident upon the surface of a film (hereinafter referred to as “film surface-reflectance”) are plotted as ordinate and the number of film-forming steps as abscissa. The transmittance, phase difference and film surface-reflectance are those determined using light rays having a wavelength A of 365 nm. In this respect, the rate of change (%) is defined by the following equation:

Rate of Change (%)=[(V_(m)−V_(in))/V_(in)]×100  (1)

[0058] wherein V_(im) represents the value observed after the immersion, V_(in) represents the value observed prior to the immersion.

[0059] FIGS. 8 to 11 each is a diagram showing the results obtained by analyzing the film composition of Sample No. 1, 2 or 4 or Sample No. 26 (reference example) listed in Table 7, using an Auger electron spectrometer. In these figures, the content of each element (arbitrary scale) is plotted as ordinate and the sputtering time (min), i.e. the position in the direction along the thickness, as abscissa. In this respect, Sample No. 26 is a uniform film formed using the usual batch type film-forming device and is given for the purpose of comparison.

[0060] The results plotted on FIGS. 8, 9 and 10 clearly indicate that the film composition can be equalized in the direction of the film thickness as the number of film-forming steps increases. The results listed in Table 3 and plotted on FIG. 6 indicate that the phase difference values as calculated on the basis of such an assumption that the film is a uniform monolayer one approach the practically measured ones as the number of film-forming steps increases and this clearly reflects the fact that the film composition is equalized in the direction of the film thickness along with the number of film-forming steps.

[0061] To clarify this fact, the non-uniform film shown in FIG. 8 is assumed to be one comprising three layers as shown in FIG. 2 for the sake of simplification and each layer is assumed to be a uniform one having a composition represented by A, B or C. More specifically, assuming that the film formed by the combination of the forward and backward movements as used shown in FIGS. 9 and 10 be constituted by three layers of uniform films which are formed by each single passage (i.e. 1 forward or backward movement) like the non-uniform film as shown in FIG. 5 and further that films have a variety of structures shown in Table 4 corresponding to the samples listed in Table 1, the reflectance, transmittance, phase difference or the like are calculated for these films. Table 5 shows the results obtained by the calculation. More specifically, Table 5 shows the optical constants and phase difference which are compared with one another and which are calculated by the RT method while assuming that each film is a uniform monolayer one although it is practically a non-uniform film. FIGS. 12, 13 and 14 are graphs showing the results listed in Table 5. The results plotted on these figures clearly indicate that the optical constants and phase difference values which are calculated on the basis of the supposition that each sample is a uniform monolayer film tend to approach the correct values as the number of film-forming steps increases. In FIG. 12, data are plotted so that they correspond to those plotted on FIG. 6.

[0062] The data plotted on FIG. 7 clearly indicate that the resistance to chemicals of the sample, which is prepared by repeating film-forming steps over less than 4 times, as determined by a test wherein the sample is immersed in a 0.5% aqueous ammonia is considerably inferior to that observed for the sample prepared by repeating the film-forming steps over not less than 4 times.

[0063] This is because the film formed comprises a considerably thick layer of molybdenum silicide oxynitride, which is susceptible to aqueous ammonia, formed on the film if the number of film-forming steps is small, as shown in FIG. 8 and if the layer is eroded by aqueous ammonia, the whole of the film is greatly affected by the erosion.

[0064] If the number of film-forming steps increases, the resistance to chemicals (in this case, aqueous ammonia) of the resulting film would be improved as will be seen from the data plotted on FIGS. 9 and 10, since the entire film is only slightly affected by the erosion of the oxynitride layer present on the film with aqueous ammonia because of the small thickness of the oxynitride layer as compared with that of the entire film and in other words, a layer having a small content of oxynitride and having high resistance to aqueous ammonia is exposed when the surface layer of the film is eroded and the erosion does not proceed any further and does not reach the interior of the film.

EXAMPLE 2

[0065] Table 6 shows conditions for producing a variety of samples each having a periodic structure. The samples were produced by repeating the forward movement of the substrate using a sputtering device which differs from that used in Example 1, but has a construction identical to that shown in FIG. 1 and can undergo the same operations as shown in FIG. 1. The structures of the sample Nos. 21 and 22 correspond to those shown in FIGS. 2 and 4 respectively. Sample Nos. 23, 24 and 25 are those produced by repeating the film-forming steps over 8, 10 and 12 times (the forward movements), respectively. Sample Nos. 31 to 35 are films produced under the same conditions used for producing the sample Nos. 21 to 25 respectively, except for conditions for annealing.

[0066] Table 7 shows the results obtained by inspecting the samples listed in Table 6 for the film thickness, i-line phase difference, spectral reflectance and spectral transmittance.

[0067] Table 8 shows i-line optical constants determined by the so-called RT method based on the measured results shown in Table 7 together with the phase difference values calculated from the optical constants thus obtained and the film thicknesses for the purpose of comparison with the practically measured values.

[0068]FIG. 15 is a graph showing the phase difference values shown in Table 8 and calculated from the optical constants of the film based on the production conditions listed in Table 6 and the film thicknesses while comparing these values with the practically measured results. In FIG. 15, the phase difference is plotted as ordinate and the number of film-forming steps as abscissa.

[0069]FIGS. 16 and 17 each is a graph showing the results obtained in the 90 minute-immersion test wherein the samples Nos. 21 to 25 and the sample is Nos. 31 to 35 listed in Table 6 were immersed in a 0.5% aqueous ammonia for 90 minutes. In these figures, the rates of change (%) in the transmittance, phase difference and film surface-reflectance are plotted as ordinate and the number of film-forming steps as abscissa. In this respect, the rate of change (%) is defined by the foregoing equation (1).

[0070] As has been described above, it would be expected from the results shown in FIGS. 8, 9 and 10 that the film composition is equalized in the direction of the film thickness as the number of film-forming steps increases. The results listed in Table 8 and plotted on FIG. 15 indicate that the phase difference values as calculated on the basis of such an assumption that the film is a uniform monolayer one approach the practically measured ones as the number of film-forming steps increases. This clearly reflects the fact that the film composition is equalized in the direction of the film thickness along with the number of film-forming steps.

[0071] These optical properties observed in this case can be explained in the same way as has already been discussed above in Example 1.

[0072] The result plotted on FIG. 16 clearly indicate that the resistance to chemicals of the sample, which is prepared by repeating the film-forming steps over less than 4 times, as determined by a test wherein the sample is immersed in a 0.5% aqueous ammonia is considerably inferior to that observed for the sample prepared by repeating the film-forming steps over not less than 4 times. The resistance to chemicals can also be explained in the same way as has already been described above in Example 1.

EXAMPLE 3

[0073] Table 9 shows conditions for producing a variety of samples each having a periodic structure. The samples are produced by repeating the forward and backward movements of the substrate using the same sputtering device as used in Example 1 and shown in FIG. 1. In Table 9, the term “for 1st layer” or “for 2nd layer” appearing on the column entitled “Purpose of Film” corresponds to each layer of the quasi-bilayered film sample in Example 4 as will be detailed below. Sample Nos. 41 to 44, Sample Nos. 45 to 47, Sample Nos. 51 to 54 and Sample Nos. 55 to 56 are produced by changing the number of film-forming steps and the substrate-conveying speed in such a manner that the ratio of the former to the latter is constant in order to make the film thickness constant in each of these sample groups.

[0074] Table 10 shows the results obtained by inspecting the samples listed in Table 9, which are not annealed after the film formation, for the film thickness, phase difference (hereinafter referred to as “KrF-phase difference”) observed for the KrF-excimer laser-exposure wavelength (hereinafter referred to as simply “KrF-exposure wavelength”) (248 nm), i-line phase difference (365 nm), spectral reflectance and spectral transmittance.

[0075] Table 11 shows the optical constants observed for the KrF-exposure wavelength (248 nm) and i-lines (365 nm) and determined by the so-called RT method based on the measured results shown in Table 10 together with the phase difference values calculated from the optical constants thus obtained and the film thicknesses for the purpose of comparison with the practically measured values.

[0076] Table 12 shows the results obtained in a 60 minute-immersion test wherein the samples listed in Table 9 were immersed in a 0.5% aqueous ammonia for 60 minutes and those observed in a 60 minute-immersion test wherein the samples are immersed in sulfuric acid-peracid (sulfuric acid/hydrogen peroxide=1/1 (% by weight)) maintained at 100° C., in terms of the transmittance values and measured phase difference values observed before and after the treatment, and the rates of change (%) in transmittance and phase difference. In this respect, the rate of change (%) is defined by the foregoing equation (1).

[0077] The film structures of the products obtained in Example 3 and the following Example 4 approximately correspond to the uniform monolayer film and the uniform bilayer film disclosed in J.P. KOKAI No. Hei 8-74031.

[0078] As has been discussed above, it would be expected from the data shown in FIGS. 8, 9 and 10 that the film composition is equalized in the direction of the film thickness as the number of film-forming steps increases, as in Example 1. The results listed in Table 11 and obtained by analyzing the samples produced under the conditions shown in Table 9 without annealing clearly indicate that, in the sample Nos. 41 to 44, Sample Nos. 45 to 47, Sample Nos. 51 to 54 and Sample Nos. 55 to 56, the optical constants as determined from the measured results listed in Table 10 within each sample group according to the RT method and the calculated phase difference values fall within the ranges which are not affected by the number of film-forming steps. This is the result naturally expected from the data obtained in Example 1 and plotted on FIGS. 6, 12, 13 and 14 and reflects the fact that the film composition is equalized in the direction along the film thickness as the number of film-forming steps increases to thus form a uniform monolayer film and an equivalent quasi-uniform monolayer film.

[0079] These optical properties observed in this case can be explained in the same way as has already been discussed above in Example 1.

[0080] The results observed for the sample Nos. 41 to 47 for the first layer listed in Table 12 clearly indicate that the films are considerably inferior in the resistance to chemicals as determined by immersing them in a 0.5% aqueous ammonia for 60 minutes and in a sulfuric acid-peracid mixture of 100° C. for 60 minutes, even if the number of film-forming steps is not less than 8 times. This would be resulted from the film-forming conditions per se for these samples listed in Table 9 and it has been known that even a uniform film is sometimes inferior in the resistance to chemicals (see, for instance, J.P. KOKAI No. Hei 8-74031 described above).

[0081] The results observed for the sample Nos. 51 to 56 for the second layer listed in Table 12 clearly indicate that the films have practically acceptable resistance to chemicals as determined by immersing them in a 0.5% aqueous ammonia for 60 minutes and in a sulfuric acid-peracid mixture of 100° C. for 60 minutes, if the number of film-forming steps is not less than 8 times and there has also been known that the uniform films per se formed according to the film-forming conditions for these samples listed in Table 9 have good resistance to chemicals.

[0082] These films would have good resistance to chemicals for the same reason discussed above in Example 1 (see, for instance, J.P. KOKAI No. Hei 8-74031 described above).

EXAMPLE 4

[0083] Table 13 shows film-forming conditions for a variety of samples each having a periodic structure which is produced by repeating the forward and backward movements using the sputtering device used in Example 1 and shown in FIG. 1. All of the samples listed in Table 13 are films of the type shown in FIG. 5 and each film was formed by repeating the film-forming steps over 8 to 12 times. In Table 13, first and second layers listed in the column entitled “Layer” correspond to the first and second layers listed in the column entitled “Purpose of Film” in Table 9, respectively and they have almost the same film compositions as those for the latter.

[0084] Table 14 shows the results of the film thickness, KrF-phase difference, i-line phase difference, spectral reflectance and spectral transmittance determined for the samples listed in Table 13 which were not subjected to any annealing treatment after the film formation.

[0085] Table 15 shows the KrF-exposure wavelength and i-line optical constant, which were calculated on the basis of the measured results listed in Table 14 according to the so-called RT method, together with the results of comparison of the phase differences calculated from the optical constants thus determined and the film thicknesses with the values practically found.

[0086] Table 16 shows the results of the 60 minute-immersion test in a 0.5% aqueous ammonia and those of the 60 minute-immersion test in a sulfuric acid-peracid at 100° C. for each sample listed in Table 13, as expressed in terms of the transmittance values, measured phase difference values and the rates of change defined by the foregoing formula (1) as determined before and after the treatment.

[0087] The first and second layers of each sample listed in Table 13 are formed by the same method used for obtaining each corresponding layer in Example 1 or 3 and therefore, it would be expected that the film composition is uniformized in the direction along the film thickness as the number of film-forming steps increases as in Example 1. The analysis results shown in Table 14 observed for the annealing-free samples listed in Table 13 clearly indicate that the optical constants as determined by the RT method and the calculated values of phase difference lie in the area which is independent of the number of film-forming steps. This is the result necessarily predicted on the basis of the results obtained in Example 1 and shown in FIGS. 6, 12, 13 and 14 and reflects the fact that the film composition is uniformized in the direction along the film thickness as the number of film-forming steps increases to thus form a film identical to a uniform monolayer film.

[0088] The optical characteristics of this film may be explained according to the same way used for the explanation of those observed for the quasi-uniform monolayer film in Example 1 and accordingly, the details thereof are herein omitted.

[0089] It has already been discussed above in Example 3 that the sample Nos. 41 to 47 for the first layer listed in Table 12 are considerably inferior in the resistance to chemicals as determined by the 60 minute-immersion test performed using a 0.5% aqueous ammonia and the 60 minute-immersion test performed using a sulfuric acid-peracid mixture maintained at 100° C., even if the number of film-forming steps is not less than 8 times, while the sample Nos. 61 to 67 of this Example exhibit practically acceptable resistance to chemicals as will be seen from the data listed in Table 16. This can be interpreted as follows: the first layer of each sample in this Example is inferior in the resistance to chemicals, but the first layer is protected by a film having the same quality as that of the second layer of the sample Nos. 51 to 56 listed in Table 12, which has good resistance to chemicals as has been discussed above in Example 3 (see, for instance, J.P. KOKAI No. Hei 8-74031 described above).

EXAMPLE 5

[0090] A phase-shifting photomask blank having the same structure as shown in FIG. 18(A) was prepared by forming a phase-shifter film, on a transparent quartz substrate, having a thickness of 150 nm, an i-line phase difference of about 180 deg. and a transmittance of 6% under approximately the same film-forming conditions as those described above in Example 1 in connection with the sample No. 4 listed in Table 1 according to the same method as used in Example 1. The resulting phase-shifting photomask blank comprises a molybdenum silicide oxynitride film (MoSiON) 104 deposited on the quartz substrate 101.

[0091] Then a resist for electron beam-exposure (such as ZEP-810S (registered trade mark in Japan), available from Nippon Zeon Co., Ltd.) was applied onto the molybdenum silicide oxynitride film 104 as shown in FIG. 18(B), while using the resulting phase-shifting photomask blank to thus give a resist film 105 having a thickness of 5000 nm. Moreover, the molybdenum silicide oxynitride film does not possess any electrical conductivity and is accordingly charged when subjecting it to electron beam-exposure without any treatment. For this reason, a nonmetallic antistatic film 106 (Espacer 100 (registered trade mark in Japan), available from Showa Denko K.K.) was formed in a thickness of about 100 Å on the oxynitride film.

[0092] Thereafter, the resist film was subjected to electron beam-exposure, followed by removal of the foregoing antistatic film 106 through water-washing and simultaneous development of the resist film 105 as shown in FIG. 18(C) to thus form a resist pattern 107.

[0093] The foregoing phase-shifting film 104 was etched, through the foregoing resist pattern 107 as a mask, by reacting the film with a mixture of CF₄ gas (flow rate: 100 sccm) and O₂ gas (flow rate: 5 sccm) as a reactive gas in a parallel plate RF ion etching system operated under conditions of an electrode-electrode space of 60 mm and a working pressure of 0.4 Torr for 3 minutes to thus form, on the quartz substrate 101, a circuit pattern 108 to be transferred onto a semiconductor substrate, as shown in FIG. 18(D). Then the foregoing resist pattern 107 was removed to give a phase-shifting photomask 115 having a structure as shown in FIG. 18(E).

EXAMPLE 6

[0094] A phase-shifting film having a thickness of 150 nm was formed on a transparent quartz substrate under approximately the same film-forming conditions as those described above in Example 4 in connection with the sample No. 65 listed in Table 13 according to the same method as used in Example 4 and then annealed at 350° C. for 3 hours to thus form a phase-shifting photomask blank having the structure shown in FIG. 19 and having a KrF-phase difference of about 180 deg. and a transmittance of 6%. The resulting phase-shifting photomask blank comprises a molybdenum silicide oxynitride (MoSiON) films 104 (first layer) and 102 (second layer) deposited on the quartz substrate 101.

[0095] Then a phase-shifting photomask 215 having a circuit pattern 108′ as shown in FIG. 20 was prepared from the resulting phase-shifting photomask blank according to the same method as used in Example 5. The phase-shifting photomask 215 thus prepared comprises a first MoSiON film 104′ and a second MoSiON film 102′ deposited on the quartz substrate 101 as well as an opening 110.

EXAMPLE 7

[0096] There was first formed a phase-shifting photomask blank which comprised a molybdenum silicide oxynitride (MoSiON) film as a phase shifter film 104 deposited on a quartz substrate 101 according to the same method as used in Example 5, as shown in FIG. 22(A) and then a resist film 105 (in this case, a photoresist film) was formed on the phase shifter film 104 in a thickness of about 5000 Å.

[0097] Then, the resist film 105 was exposed to i-lines, followed by development of the resist film 105 as shown in FIG. 22(B) to give a resist film 107 carrying a desired resist pattern.

[0098] Thereafter, a phase-shifting photomask 115 having a structure as shown in FIG. 22(D) was prepared by subjecting the phase shifter film 104 to RF ion etching through the foregoing resist film 107 as a mask in the same manner as used in Example 5 and then removing the resist pattern 107 as shown in FIG. 22(C).

EXAMPLE 8

[0099] In this Example, the steps for the manufacture of a phase-shifting photomask will be described while referring to the accompanying FIGS. 23(A) to 23(E). First, a phase-shifting photomask blank having a structure as shown in FIG. 23(A) was prepared according to the same method as used in Example 5. More specifically, a metallic antistatic film 106′ which consisted of a molybdenum film having a thickness of about 100 to 500 Å was formed on a phase-shifter film 104 deposited on a quartz substrate 101 and then a resist film 105 for electron beam-exposure was formed on the metallic antistatic film 106′ in a thickness of 5000 Å. The molybdenum film was formed according to the usual DC magnetron sputtering method using a molybdenum target. This is because the phase-shifter film 104 does not have electrical conductivity.

[0100] Then, as shown in FIG. 23(B), the desired portions of the resist film 105 was subjected to electron beam-exposure, followed by development thereof to form a resist film 107 carrying a desired resist pattern.

[0101] Thereafter, the metallic antistatic film 106′ and the phase-shifter film 104 were subjected to RF ion etching through the resist film 107 for electron beam-exposure as a mask according to the same method as used in Example 5, as shown in FIG. 23(C).

[0102] Next, the resist film pattern 107 was removed by, for instance, the O₂ plasma etching technique as shown in FIG. 23(D), followed by removal of the metallic antistatic film 106′ by etching the film with an etching liquid (H₂SO₄+H₂O₂) as shown in FIG. 23(E) to thus give a phase-shifting photomask 115 having a structure shown in FIG. 23(E).

EXAMPLE 9

[0103] A resist film 105 was formed according to the same method as used in Example 8 and then a nonmetallic antistatic film 106 (aqua SAVE-53za, available from Nitto Chemical Industry Co., Ltd.) was formed on the resist film 105 in a thickness of about 500 to 1000 Å, prior to the electron beam exposure, as shown in FIG. 24(A). Thereafter, the resist film was exposed to electron beam, followed by removal of the nonmetallic antistatic film 106 through water-washing simultaneous with the development of the resist film 105 to give a resist pattern 107 as shown in FIG. 24(B). Then the same procedures as shown in FIGS. 23(B) to 23(E) and used in Example 8 were repeated to form a phase-shifting photomask 115.

[0104] In the foregoing Examples, only one cathode 32 of the film-forming device was used, but another cathode (not shown) adjacent to the cathode 32 and having the same structure as that of the latter may simultaneously be used so that a substrate passes over these two cathodes during a single film-forming step. Moreover, only one cathode 32 was used also in Examples 3 and 4, but a cathode other than the cathode 32 may be used in such a manner that the first film as shown in Tables 9 and 10 is, for instance, formed using one cathode 32, while the second film is formed using the other cathode.

[0105] In the foregoing Examples, molybdenum is used as a constituent element or metal for the substance constituting the phase-shifting portion of the optically semitransparent part, but the constituent element is not restricted to the same and may be those commonly used in this field such as Ta or W.

[0106] In the foregoing Examples 7 to 9, only the phase-shifter having the monolayered structure as shown in FIG. 18(A) was described, but those having a bi-layer structure as shown in FIG. 19 may likewise be used without any problem.

[0107] In Examples 8 and 9, a molybdenum film was used as the metallic antistatic film 106′. However, the latter is not limited to the former and may be any other metal film which can ensure the achievement of the same effect such as films of, for instance, Cr, W, Ta, Ti, Si, Al and alloys thereof.

[0108] In the foregoing Examples, argon gas was used as the inert gas. However, the inert gas may be any inert gas other than argon such as helium, neon, krypton and xenon. In addition, NO gas was used as the reactive gas, but it is also possible to use N₂O gas or a mixed gas comprising N₂ gas and O₂ gas.

[0109] In the foregoing Examples, the quartz substrate was used as a substrate for forming films, but it is a matter of course that the other transparent substrates may be used instead.

[0110] According to the present invention, a film is formed by passing a substrate for film-formation over a target at least 4 times and this permits the formation of a thin film having a periodic structure which consists of at least 4 unitary nonuniform films each formed, on the substrate, through a single film-forming step. More specifically, the present invention permits the formation of a substantially uniform film which has optical characteristics quite similar to those which would be observed for the uniform monolayer film and which has resistance to chemicals substantially comparable to that observed for the uniform film, without sacrificing or impairing the utilization efficiency of the target and the productivity rate. In other words, the resulting film of the present invention having a periodic structure can substantially be handled as a monolayer film, this makes the calculation of optical constants, film design and quality control of the film quite easy and accordingly, the present invention makes the production of a phase-shifting photomask blank and phase-shifting photomask quite easy. TABLE 1 (Example 1: Forward Movement and Forward and Backward Movements) Ar NO Film- Sputter- Sputter- Number Flow Flow Forming ing ing of Film- Conveying Sample Rate Rate Pressure Current Voltage Forming Speed Annealing No. SCCM SCCM mTorr A V Steps mm/min Conditions Remark 1 80 35 4.2 1.5 (˜450) 1 90 250° C., 1 hr 1 Forward Movement 2 80 35 4.2 1.5 ″ 4 90 × 4 = 360 250° C., 1 hr 2 Forward and Backward Movements 3 ″ ″ ″ ″ ″ 6 90 × 6 = 540 ″ 3 Forward and Backward Movements 4 ″ ″ ″ ″ ″ 8 90 × 8 = 720 ″ 4 Forward and Backward Movements 5 ″ ″ ″ ″ ″ 12  90 × 12 = ″ 6 Forward 1080 and Backward Movements

[0111] TABLE 2 (Example 1: Optical Characteristic Properties; Annealing at 250° C. for one hour; Forward Movement and Forward and Backward Movements) Film i-Line Thick- Phase Spectral Characteristic Properties Sample ness Difference Wave- No. nm deg. length nm 240 248 260 350 365 380 420 436 450 1 152.5 180.41 Reflec- % 10.24 10.33 10.42 10.34 10.69 11.19 12.57 12.89 13.0 tance Trans- % 0.5 0.7 1.0 5.6 6.9 8.1 11.3 12.6 13.7 mittance 2 152.5 178.01 Reflec- % 21.13 21.18 21.12 17.86 17.77 17.99 19.45 20.00 20.33 tance Trans- % 0.5 0.6 0.9 5.0 6.0 7.1 10.0 11.1 12.1 mittance 3 150.0 177.92 Reflec- % 18.27 17.99 17.64 16.01 16.40 17.10 19.39 20.14 20.58 tance Trans- % 0.4 0.6 0.9 5.2 6.2 7.3 10.1 11.2 12.1 mittance 4 150.0 178.21 Reflec- % 17.11 17.04 17.07 16.16 16.56 17.22 19.52 20.28 20.75 tance Trans- % 0.4 0.6 0.9 5.4 6.1 7.2 10.0 11.0 12.0 mittance 5 149.0 176.44 Reflec- % 16.78 16.81 16.83 16.05 16.50 17.25 19.62 20.34 20.75 tance Trans- % 0.5 0.7 1.0 5.4 6.5 7.6 10.4 11.5 12.5 mittance

[0112] TABLE 3 (Example 1: λ = 365 nm; Annealing at 250° C. for one hour; Forward Movement and Forward and Backward Movements) Film Thickness Phase Phase Number of Used For Difference Difference Sample Film-Forming Calculation Optical Constant (Found) (Calculated) No. Steps nm n k deg. deg. 1 1 151 1.644 0.4993 180.41 92.92 2 4 151 2.320 0.4962 178.01 192.8 3 6 152.5 2.182 0.4922 177.92 173.81 4 8 152 2.191 0.4961 178.21 174.68 5 12 151 2.186 0.4881 176.44 172.66

[0113] TABLE 4 (Explanation of Example 1: λ = 365 nm) Film Thick- Number Film ness per of Film- Film Single Form Num- Thick- Film- Averaged ing ber of Optical ness Forming Optical Steps Layers Constitution of Constant d_(j) Step 152.5/ Constant VN V Film n_(j) k_(j) nm VN nm <n> <k> Remark 1 3 Air Air 1.0 0.0 — — — — Film Constitutions Layer C 2.022 0.3940 48.50 152.5/1 2.220 0.4780 are abbreviated as Layer B 2.330 0.5347 76.86 CBA. Layer A 2.264 0.4673 27.15 Subst- QZ 1.475 0.0 — — — — rate 2 6 A 2.264 0.4673 13.57 152.5/2 2.220 0.4780 Film Constitutions B 2.330 0.5347 38.43 are abbreviated as C 2.022 0.3940 24.25 ABC/CBA. C 2.022 0.3940 24.25 B 2.330 0.5347 38.43 A 2.264 0.4673 13.57 3 9 CBA/ABC/CBA 152.5/3 2.220 0.4780 The optical constant of each layer is the 4 12 (ABC/CBA)² 152.5/4 ″ ″ same as that observ ed for each corres- 6 18 (ABC/CBA)³ 152.5/6 ″ ″ ponding layer A,B, C when VN = 1 in 8 24 (ABC/CBA)⁴ 152.5/8 ″ ″ case of layers A,B,C. The layer thickness 10 30 (ABC/CBA)⁵ 152.5/10 ″ ″ of the layer A, B or C is the value corre 12 36 (ABC/CBA)⁶ 152.5/12 ″ ″ sponding to the layer- thickness observed 14 42 (ABC/CBA)⁷ 152.5/14 ″ ″ when VN = 1, divided by VN. 16 48 (ABC/CBA)⁸ 152.5/16 ″ ″

[0114] TABLE 5 (Explanation of Example 1: λ = 365 nm) Number Optical Constant of Film- Num- Reflec- Trans- Determined by Phase Difference Forming ber of tance mittance Optical Constant Monolayer RT Correct Approx. Steps Layers R T Averaged Value Method Value Value VN V % % <n> <k> n k deg. deg. 1 3 10.69 6.90 2.220 0.4780 1.648 0.4944 189.7 94.52 2 6 19.79 6.45 ″ ″ 2.492 0.4673 177.1 221.2 3 9 14.60 6.51 ″ ″ 1.972 0.4914 178.9 142.4 4 12 16.71 6.99 ″ ″ 2.217 0.4935 182.0 179.1 6 18 15.65 6.48 ″ ″ 2.094 0.4872 181.0 160.8 8 24 16.14 6.49 ″ ″ 2.161 0.4839 180.6 170.7 10 30 16.33 6.49 ″ ″ 2.186 0.4827 180.5 174.6 12 36 16.43 6.49 ″ ″ 2.199 0.4822 180.5 176.6 14 42 16.48 6.49 ″ ″ 2.206 0.4819 180.4 177.6 16 48 16.52 6.49 ″ ″ 2.211 0.4817 180.4 178.3

[0115] TABLE 6 (Example 2: Forward Movement) Film- Ar Flow NO Flow Forming Sputtering Sputtering Number of Conveying Sample Rate Rate Pressure Current Voltage Film-Form- Speed Annealing No. SCCM SCCM mTorr A V ing Steps mm/mm Conditions 21 190 6.5 ˜4 0.67 386 1 35 250° C., 1 hr 22 190 6.5 ˜4 0.67 388 4 35 × 4 = 140 250° C., 1 hr 23 ″ ″ ″ ″ 383 8 35 × 8 = 280 ″ 24 ″ ″ ″ ″ 383 10 35 × 10 = 350 ″ 25 ″ ″ ″ ″ 383 12 35 × 12 = 420 ″ 31 190 6.5 ˜4 0.67 386 1 35 350° C., 3 hrs 32 190 6.5 ˜4 0.67 388 4 35 × 4 = 140 350° C., 3 hrs 33 ″ ″ ″ ″ 383 8 35 × 8 = 280 ″ 34 ″ ″ ″ ″ 383 10 35 × 10 = 350 ″ 35 ″ ″ ″ ″ 383 12 35 × 12 = 420 ″

[0116] TABLE 7 (Example 2: Optical Characteristic Pro erties; Annealing at 250° C. for one hour (Sample Nos. 21-26); Annealing at 350° C. for 3 hours (Sample Nos. 31-36); Forward Movement) i-Line Film Phase Sam- Thick- Differ- ple ness ence Spectral Characteristic Properties No. nm deg. Wavelength nm 248 350 365 389 420 436 450 488 546 21 ˜ 158.46 Reflectance % 6.69 10.08 10.73 11.18 11.11 10.56 9.90 7.65 4.56 139 Transmittance % 1.2 7.6 8.9 10.1 13.5 14.9 16.2 19.8 25.4 22 ˜ 163.95 Reflectance % 15.39 15.16 15.78 16.65 18.91 19.51 19.79 19.46 16.89 150 Transmittance % 0.9 6.1 7.2 8.2 11.0 12.0 13.0 15.5 19.6 23 ˜ 160.61 Reflectance % 14.93 14.76 15.53 16.44 18.47 18.85 18.98 18.27 15.52 150 Transmittance % 1.1 6.8 8.0 9.1 11.9 13.1 14.1 16.7 21.4 24 ˜ 162.76 Reflectance % 15.50 15.13 15.79 16.62 18.60 19.01 19.16 18.57 15.95 150 Transmittance % 0.9 6.2 7.3 8.4 11.1 12.6 13.2 15.8 20.0 25 ˜ 161.71 Reflectance % 14.26 13.80 14.44 15.22 17.05 17.38 17.47 16.90 14.36 150 Transmittance % 1.1 7.2 8.3 9.4 12.4 13.6 14.5 17.3 21.8 26 ˜ 180.50 Reflectance % 14.90 14.09 14.13 14.56 17.00 18.08 18.88 19.98 18.63 (Ref) 168 Transmittance % 0.7 6.3 7.6 8.9 12.2 13.4 14.4 17.1 21.5 31 ˜ 149.48 Reflectance % 10.87 1.54 1.20 1.05 0.87 0.37 0.66 0.48 1.39 130 Transmittance % 1.9 11.1 12.8 14.4 18.7 20.4 21.9 25.8 30.9 32 ˜ 161.70 Reflectance % 9.16 10.89 11.84 12.96 15.65 16.36 16.73 16.65 14.58 150 Transmittance % 1.0 6.6 7.6 8.6 11.2 12.2 13.1 15.5 19.5 33 ˜ 160.97 Reflectance % 10.81 12.43 13.34 14.38 16.66 17.18 17.41 17.02 14.79 150 Transmittance % 1.0 6.4 7.5 8.5 11.0 12.1 12.9 15.4 19.5 34 ˜ 163.44 Reflectance % 12.24 13.15 13.95 14.88 17.03 17.53 17.78 17.40 15.13 150 Transmittance % 0.9 6.2 7.2 8.2 10.8 11.8 12.7 15.2 19.2 35 ˜ 161.41 Reflectance % 11.71 12.91 13.82 14.85 17.18 17.70 17.93 17.50 15.06 150 Transmittance % 1.1 7.0 8.1 9.1 11.9 12.9 13.8 16.4 20.7 36 ˜ 175.67 Reflectance % 10.77 10.99 11.32 12.03 14.82 15.84 16.54 17.26 15.56 (Ref) 168 Transmittance % 1.1 7.9 9.4 10.8 14.3 15.6 16.7 19.6 24.3

[0117] TABLE 8 (Example 2 Annealing at 250° C. for one hour) Film Thick- Number of ness Used For Phase Difference Film-Forming Calculation Optical Constant (Found) (Calculated) Sample No. Steps nm n k deg. deg. 21 1 150 1.682 0.4504 158.46 98.06 22 4 150 2.095 0.4757 163.95 158.17 23 8 150 2.085 0.4546 160.61 156.81 24 10 150 2.099 0.4728 162.70 158.80 25 12 157 2.060 0.4304 161.71 160.80 26 (Ref) — 168 2.108 0.4154 180.50 180.60

[0118] TABLE 9 (Example 3: Film-Forming Conditions for Quasi-Monolayer Film for KrF 6%; Forward and Backward Movements) Number of Convey- Flow Rate Film-Form- ing Sample Purpose of Ar NO Pressure Current Voltage ing Steps Speed No. Film SCCM SCCM mTorr A V × 2 mm/min Annealing 41 For 1st Layer 150  34 5.7 2 524 4 360 Not An- 42 ″ ″ ″ 5.8 ″ 524 6 540 nealed 43 ″ ″ ″ 5.7 ″ 525 8 720 and An- 44 ″ ″ ″ 5.7 ″ 526 12 1080  nealed at 305° C. for 3 hours. 45 ″ 150  42.5 5.8 3 567 4 520 Not An- 46 ″ ″ ″ 6.0 ″ 566 6 780 nealed 47 ″ ″ ″ 6.0 ″ 565 8 1040  and An- nealed at 305° C. for 3 hours. 51 For 2nd Layer 30 8.4 1.2 0.5 504 4 400 Not An- 52 ″ ″ ″ 1.1 ″ 503 6 600 nealed 53 ″ ″ ″ ˜1 ″ 502 8 800 and An- 54 ″ ″ ″ 1.2 ″ 504 12 1200  nealed at 305° C. for 3 hours. 55 ″ 30 20 0.96 ″ 572 4 880 Not An- 56 ″ ″ ″ ˜1 ″ 569 6 1320  nealed and An- nealed at 305° C. for 3 hours.

[0119] TABLE 10 (Example 3: Optical Characteristics of the annealing-free product for KrF 6%; Forward and Backward Movements) Phase Difference Wavelength Film (nm) Spectral Reflectance (R) and Spectral Transmittance (T) Sample Thickness 248 365 Wavelength (nm) No. nm deg. deg. 240 248 260 350 365 380 420 436 450 488 Remarks 41 (88) 113.4 76.69 R % 14.34 14.07 13.45 7.92 7.96 8.35 10.54 11.69 12.73 15.43 The number in T % 16.42 18.20 20.99 42.05 44.92 47.62 53.10 54.78 56.00 58.58 the parenthesis 42 (89) 114.9 80.19 R % 14.45 14.23 13.66 7.99 8.00 8.35 10.52 11.68 12.74 15.51 indicates the T % 15.85 17.55 20.22 40.83 43.73 46.40 51.20 53.67 54.95 57.47 film thickness 43 (89) 114.9 80.78 R % 14.41 14.20 13.65 7.97 7.98 8.35 10.56 11.75 12.81 15.61 determined by T % 15.98 17.69 20.42 41.33 44.23 46.97 52.55 54.23 55.52 58.04 analytical 44 (91) 112.5 79.24 R % 13.80 13.65 13.25 7.66 7.63 7.96 10.18 11.37 12.44 15.26 method T % 16.78 18.55 21.32 42.47 45.27 47.93 53.27 54.90 56.07 58.53 45 80 — 82.62 R % 14.21 14.04 13.58 8.07 7.95 8.13 9.97 11.05 12.06 14.88 T % 14.6 16.2 18.7 38.2 41.2 44.0 50.0 51.9 53.3 56.2 46 91 — — R % 14.67 14.68 14.35 8.41 8.04 8.00 9.40 10.39 11.37 14.17 T % 15.6 17.3 19.9 40.2 43.3 45.9 51.6 53.4 54.3 57.3 47 92 — — R % 14.10 14.27 14.28 8.52 7.95 7.78 8.90 9.84 10.78 13.60 T % 14.0 15.5 18.0 37.7 41.1 44.0 50.7 53.2 54.3 57.4 51 40 55.8 41.51 R % 22.39 23.13 24.29 30.28 30.74 31.04 31.37 31.36 31.26 30.90 T % 20.8 22.2 24.0 33.9 35.2 36.3 38.9 39.9 40.7 42.8 52 41 56.7 41.77 R % 23.48 24.14 25.30 31.18 31.63 31.94 32.30 32.29 32.24 31.88 T % 19.4 20.7 22.5 32.1 33.2 34.3 36.9 37.8 38.6 40.6 53 40 55.4 42.26 R % 23.63 24.36 25.43 31.37 31.85 32.19 32.60 32.63 32.58 32.24 T % 18.9 20.2 22.0 31.4 32.5 33.6 36.1 37.1 37.8 39.9 54 40 55.6 41.81 R % 22.54 23.35 24.54 30.73 31.21 31.53 31.96 31.97 31.90 31.56 T % 20.2 21.5 23.3 33.0 34.2 35.2 37.8 38.8 39.5 41.6 55 38 — 42.82 R % 21.73 22.41 23.51 30.12 30.67 31.07 31.66 31.74 31.71 31.49 T % 19.4 20.8 22.6 32.5 33.7 34.7 37.4 38.3 39.1 41.2 56 38 — 43.54 R % 22.24 22.86 23.96 30.58 31.14 31.57 32.18 32.27 32.28 32.08 T % 18.5 19.9 21.7 34.1 32.5 33.5 36.1 36.9 37.7 39.7

[0120] TABLE 11 (Example 3: Optical Characteristics and Phase Difference of the Annealing-Free Quasi-Monolayer Film for KrF 6%) Number of Film- Wavelength (nm) Form- Film 248 365 Pur- ing Thick Optical Phase Difference Optical Phase Difference Sample pose of Steps × ness Constant Found Calculated Constant Found Calculated No. Film 2 nm n k Deg. deg. n k deg. deg. 41 For 4 88 1.913 0.3440 113.4 114.4 1.883 0.2313 79.69 75.17 42 1st 6 89 1.918 0.3478 114.9 116.2 1.901 0.2361 80.19 77.74 43 Layer 8 89 1.916 0.3463 114.9 116.1 1.901 0.2326 80.78 77.76 44 12 91 1.887 0.3309 112.5 114.9 1.863 0.2217 79.24 76.2 45 For 4 92 1.904 0.3554 — 118.2 1.894 0.2458 82.62 79.92 46 1st 6 91 1.937 9.3429 — 121.3 1.921 0.2326 — 81.50 47 Layer 8 92 1.916 0.3651 — 119.7 1.893 0.2466 — 79.85 51 For 4 36.3 2.190 0.7148 55.8 55.57 2.312 0.5614 41.51 41.30 52 2nd 6 35.8 2.236 0.7572 56.7 56.67 2.346 0.6089 41.77 41.39 53 Layer 8 35.6 2.224 0.7769 55.4 55.54 2.361 0.6126 42.26 42.75 54 12 36.2 2.189 0.7349 55.6 55.18 2.330 0.5851 41.81 41.32 55 For 4 37.7 2.216 0.7236 — 59.48 2.316 0.5809 42.82 42.80 2nd 56 Layer 6 37.9 2.325 0.7311 — 65.66 2.339 0.6025 43.54 43.60

[0121] TABLE 12 (Example 3: Resistance to Chemicals of the Annealed Quasi-Monolayer Product for KrF 6% (Annealing at 350° C. for 3 hours)) Num- ber of Aqueous Ammonia (0.5%, 60min) Sulfuric Acid-Peracid (60min) Film- Transmittance Phase Difference Transmittance Phase Difference Form- (Wavelength: 248nm) (Wavelength: 365 nm) (Wavelength: 248 nm) (Wavelength: 365 nm) Sam- Purpose ing Prior to After Rate of Prior to After Rate of Prior to After Rate of Prior to After Tre Rate of ple of Steps Treat- Treat- Change Treatment Treatment Change Treat- Treat- Change Treatment Treatment Change No. Film × 2 ment % ment % % deg. deg. % ment % ment % % deg. deg. % 41 For 4 80.2 85.95 7.170 43.39 33.16 −23.58 81.77 89.5 9.453 41.38 38.52 −6.912 1st Layer 42 For 6 83.30 88.35 6.062 43.39 32.41 −25.30 83 90.32 8.819 41.88 38.53 −8.000 1st Layer 43 For 8 79.25 87.30 10.16 43.57 32.95 −24.37 81.55 89.99 10.35 42.3 38.6 −8.747 1st Layer 44 For 12 79.05 87.13 10.22 43.38 34.07 −21.46 79.82 90.38 13.23 42.82 37.92 −11.44 1st Layer 45 For 4 48.00 80.10 66.88 59.01 17.49 −70.36 60.08 91.62 52.50 55.31 41.73 −24.55 1st Layer 46 For 6 50.40 68.40 35.71 58.64 11.64 −80.15 67.05 91.5 36.46 54.67 43.95 −19.61 1st Layer 47 For 8 45.30 81.60 80.13 59.80 8.81 −85.27 67.77 91.67 35.27 52.71 41.62 −21.04 1st Layer 51 For 4 27.68 27.65 −0.108 39.47 39.39 −0.203 27.1 27.3 0.738 39.6 39.58 −0.050 2nd Layer 52 For 6 25.83 25.78 −0.194 39.94 39.69 −0.626 25.17 25.46 1.152 39.67 39.44 −0.580 2nd Layer 53 For 8 25.05 25.03 −0.080 39.61 39.99 0.959 24.26 24.52 1.072 39.39 39.45 0.152 2nd Layer 54 For 12 26.00 25.97 −0.115 39.75 39.72 −0.0755 25.43 25.7 1.062 40.11 39.87 −0.5984 2nd Layer 55 For 4 26.10 25.90 −0.766 41.79 41.94 0.359 25.32 25.31 −0.0395 41.59 42.07 1.154 2nd Layer 56 For 6 24.90 24.80 −0.402 41.17 41.44 0.656 23.93 23.95 0.0836 41.49 41.6 0.2651 2nd Layer

[0122] TABLE 13 (Example 4 Film-Forming Conditions for Quasi-Bilayer Film for KrF 6%; Forward and Backward Movements) Number of Film- Convey- Flow Rate Forming ing Sample Ar NO Pressure Current Voltage Steps Speed No. Layer SCCM SCCM mTorr A V ×2 mm/min Annealing 61 2nd Layer  30 9 1.0 0.5 500 4 360 Not Annealed 1st Layer 150 34 5.6 2.0 525 4 320 and Annealed at 350° C. for 3 hrs. 62 2nd Layer  30 8.4 1.0 0.550 4 6 600 Not Annealed 1st Layer 150 34 5.4 2.0 524 6 510 and Annealed at 350° C. for 3 hrs. 63 2nd Layer  30 9 1.1 0.5 502 4 380 Not Annealed 1st Layer 150 34 5.5 2.0 522 6 480 and Annealed at 350° C. for 3 hrs. 64 2nd Layer  30 9 1.0 0.5 501 6 600 Not Annealed 1st Layer 150 34 5.6 2.0 520 4 320 and Annealed at 350° C. for 3 hrs. 65 2nd Layer  30 20 1.0 1 573 4 880 Not Annealed 1st Layer 150 42.5 6.0 3 568 4 520 and Annealed at 350° C. for 3 hrs. 66 2nd Layer  30 20 1.0 1 565 6 1320 Not Annealed 1st Layer 150 42.5 6.0 3 569 6 780 and Annealed at 350° C. for 3 hrs. 67 2nd Layer  30 20 1.0 1 571 4 880 Not Annealed 1st Layer 150 42.5 ˜6 3 568 8 1040 and Annealed at 350° C. for 3 hrs.

[0123] TABLE 14 (Example 4 Optical Characteristics of the Annealing-Free Quasi-Bilayer Film for KrF 6%; Forward and Backward Movements) Phase Difference Wavelength (nm) Spectral Reflectance (R) and Spectral Transmittance (T) Sample Film 248 365 Wavelength (nm) No. Thickness (nm) deg. deg. 240 248 260 350 365 380 420 436 450 488 61 116 193.9 138.28 R % 18.08 17.96 17.95 23.87 24.96 25.67 25.78 25.21 24.51 22.22 T % 2.8 3.4 4.4 13.7 15.2 16.6 20.7 22.3 23.8 27.9 62 118 165.85 118.44 R % 21.46 21.50 21.77 24.70 24.02 23.04 19.72 18.34 17.25 15.13 T % 5.2 6.1 7.6 19.1 21.0 23.0 28.7 31.0 33.0 38.3 63 140 — — R % 19.76 19.63 19.57 24.95 26.10 26.89 27.14 26.62 25.95 23.72 T % 2.6 3.1 4.1 13.4 14.9 16.3 20.2 21.8 23.3 27.4 64  95 168.2 121.7 R % 18.48 18.59 18.98 23.86 23.70 23.18 20.58 19.32 18.24 15.86 T % 4.9 5.9 7.3 18.2 20.1 22.0 27.2 29.4 31.3 36.4 65 125 — — R % 19.19 19.22 19.46 26.06 26.60 26.72 25.60 24.76 23.99 21.98 T % 3.0 3.6 4.6 13.4 14.9 16.3 20.6 22.4 24.0 28.8 66 120 — 113.87 R % 19.10 19.46 20.34 25.08 24.74 24.15 22.16 21.43 20.90 20.30 T % 4.3 5.0 6.2 15.7 17.5 19.3 24.4 26.6 28.4 33.0 67 130 — 126.56 R % 19.08 19.10 19.42 26.03 26.37 26.30 24.82 23.89 23.11 21.18 T % 3.3 4.0 5.1 14.1 15.7 17.2 21.7 23.6 25.3 30.0

[0124] TABLE 15 (Example 4 Optical Characteristics and Phase Difference of the Annealed Quasi-Bilayer Product for KrF 6%; Forward and Backward Movements) Wavelength (nm) 248 365 Number Phase Phase of Film- Film Difference Difference Forming Thick- Optical Calcu- Optical Calcu- Sample Steps ness Constant Found lated Constant Found lated No. Layer ×2 nm n k deg. deg. n k deg. deg. 61 2nd Layer 4 41.76 2.090 0.6841 2.246 0.5733 1st Layer 4 101.24 1.913 0.3440 1.883 0.2313 Whole Layer 143 193.9 195.86 138.28 133.92 62 2nd Layer 6 33.28 2.272 0.6732 2.258 0.5123 1st Layer 6 82.72 1.918 0.3478 1.978 0.2361 Whole Layer 116 165.85 166.44 118.44 117.95 63 2nd Layer 4 38.67 2.097 0.7751 2.263 0.6114 1st Layer 6 101.33 1.918 0.3478 — 1.901 0.2361 Whole Layer 140 — 191.48 — 132.48 64 2nd Layer 6 35.28 2.136 0.6406 2.201 0.5221 1st Layer 4 86.72 1.913 0.3440 1.983 0.2317 Whole Layer 122 168.2 168.58 121.70 121.98 65 2nd Layer 4 38.95 2.132 0.7297 2.291 0.6059 1st Layer 4 95.05 1.904 0.3554 1.894 0.2458 Whole Layer 134 — 183.93 128.13 127.91 66 2nd Layer 6 35.28 2.079 0.7676 2.313 0.6440 1st Layer 6 84.72 1.937 0.3429 1.921 0.2326 Whole Layer 120 — 165.25 113.87 114.49 67 2nd Layer 4 38.51 2.177 0.6633 2.287 0.5744 1st Layer 8 93.99 1.916 0.3651 1.893 0.2446 Whole Layer 132.5 — 186.2 126.56 126.59

[0125] TABLE 16 (Example 4 Resistance to Chemicals of the Annealed (at 350° C., for 3 hours) Quasi-Bilayer Film for KrF 6%) Number Aqueous Ammonia 0.5% 60 min of Transmittance Phase Difference Film- (Wavelength: 248 nm) (Wavelength: 365 nm) Form- Prior to After Rate of Prior to After Rate of Sample ing Treatment Treatment Change Treatment Treatment Change No. Layer Steps % % % deg. deg. % 61 2nd Layer 4 5.92 5.92 0.00 189.40 189.10 −0.158 1st Layer 4 62 2nd Layer 6 10.37 10.37 0.00 159.90 159.50 −0.250 1st Layer 6 63 2nd Layer 4 5.92 5.99 1.182 190.80 190.40 −0.210 1st Layer 6 64 2nd Layer 6 9.20 9.31 1.196 161.70 162.70 0.618 1st Layer 4 65 2nd Layer 4 5.30 5.30 0.00 173.45 173.90 0.259 1st Layer 4 66 2nd Layer 6 7.70 7.70 0.00 153.45 154.30 0.554 1st Layer 6 67 2nd Layer 4 6.60 6.60 0.00 169.95 171.25 0.765 1st Layer 8 Sulfuric Acid-Peracid 60 min Transmittance Phase Difference (Wavelength: 248 nm) (Wavelength: 365 nm) Prior to After Rate of Prior to After Rate of Sample Treatment Treatment Change Treatment Treatment Change No. % % % deg. deg. % 61 6.4 6.49 1.406 185.3 185.3 0.00 62 11.29 11.43 1.240 1537 155 0.846 63 6.29 6.38 1.431 184.7 185.5 0.433 64 9.92 10.06 1.411 159.4 159.1 −0.188 65 6.95 6.94 −0.144 171.90 170.90 −0.582 66 8.24 8.23 −0.121 149.10 148.10 −0.671 67 7.28 7.29 0.137 167.30 164.50 −1.674 

What is claimed is:
 1. A method for preparing a phase-shifting photomask blank, comprising the steps of: supplying a reactive gas to a film-forming chamber; and depositing a thin film on a substrate by a reactive sputtering technique while passing said substrate over a target, wherein said thin film is formed by passing, at least 4 times, said substrate over said target.
 2. The method for preparing a phase-shifting photomask blank as set forth in claim 1 wherein NO gas is used as said reactive gas, a target composed of molybdenum and silicon is used as said target and a transparent substrate is used as said substrate to thus form, on said transparent substrate, a light-transmitting film capable of transmitting light rays having an intensity which cannot substantially contribute to exposure.
 3. The method for preparing a phase-shifting photomask blank as set forth in claim 1 wherein said thin film is formed through an opening having a sufficiently enlarged length along a substrate-conveying direction so that even regions whose deposition rate of a target component is not more than 90% of a maximum level thereof also contribute to the film-formation.
 4. The method for preparing a phase-shifting photomask blank as set forth in claim 2 wherein said thin film is formed through an opening having a sufficiently enlarged length along a substrate-conveying direction so that even regions whose deposition rate of a target component is not more than 90% of the maximum level thereof also contribute to the film-formation.
 5. A method for preparing a phase-shifting photomask, comprising the steps of: preparing a phase-shifting photomask blank according to the method for preparing a phase-shifting photomask blank as set forth in claim 1 ; and removing a part of a light-translucent film of said phase-shifting photomask blank by subjecting said film to a patterning treatment to form a pattern consisting of the resulting light-translucent portions and light-transmitting portions capable of transmitting light rays having an intensity which can substantially contribute to the exposure.
 6. A method for preparing a phase-shifting photomask, comprising the steps of: preparing a phase-shifting photomask blank according to the method for preparing a phase-shifting photomask blank as set forth in claim 2 ; and removing a part of a light-translucent film of said phase-shifting photomask blank by subjecting said film to a patterning treatment to form a pattern consisting of the resulting light-translucent portions and light-transmitting portions capable of transmitting light rays having an intensity which can substantially contribute to the exposure.
 7. The method for preparing a phase-shifting photomask as set forth in claim 5 wherein said patterning treatment of the light-translucent film of the phase-shifting photomask blank is performed by a light-exposure process which uses a light rays-exposure technique.
 8. The method for preparing a phase-shifting photomask as set forth in claim 5 wherein said patterning treatment of the light-translucent film of the phase-shifting photomask blank is performed by a light-exposure process which uses an electron beam-exposure technique.
 9. The method for preparing a phase-shifting photomask as set forth in claim 8 wherein a non-metallic antistatic film is formed on a resist film for electron beam-exposure prior to the electron beam exposure.
 10. The method for preparing a phase-shifting photomask as set forth in claim 8 wherein a metallic antistatic film is formed on a phase-shifter film formed on said substrate and then a resist for electron beam exposure is applied onto said antistatic film before the electron beam exposure.
 11. A phase-shifting photomask blank, comprising a thin film formed on a substrate by a reactive sputtering technique which is performed by supplying a reactive gas to a film-forming chamber and forming said thin film by passing said substrate over a target, at least 4 times.
 12. The phase-shifting photomask blank as set forth in claim 11 wherein NO gas is used as said reactive gas, a target composed of molybdenum and silicon is used as said target and a transparent substrate is used as said substrate to form, on said transparent substrate, a light-transmitting film capable of transmitting light rays having an intensity which cannot substantially contribute to exposure.
 13. The phase-shifting photomask blank as set forth in claim 12 wherein it comprises a thin film which is formed, on said substrate, through an opening having a sufficiently enlarged length along a substrate-conveying direction so that even regions whose deposition rate of a target component is not more than 90% of the maximum level thereof also contribute to the film-formation.
 14. The phase-shifting photomask blank as set forth in claim 11 wherein a metallic antistatic film is formed on a phase-shifter film formed on said substrate.
 15. The phase-shifting photomask blank as set forth in claim 12 wherein a metallic antistatic film is formed on a phase-shifter film formed on said substrate.
 16. The phase-shifting photomask blank as set forth in claim 13 wherein a metallic antistatic film is formed on a phase-shifter film formed on said substrate.
 17. The phase-shifting photomask blank as set forth in claim 14 wherein a resist film for electron beam-exposure is formed on said metallic antistatic film.
 18. The phase-shifting photomask blank as set forth in claim 17 wherein a nonmetallic antistatic film is formed on said resist film for electron beam-exposure.
 19. The phase-shifting photomask blank as set forth in claim 11 wherein a nonmetallic antistatic film is formed on the phase-shifter film formed on said substrate through a resist film for electron beam-exposure.
 20. The phase-shifting photomask blank as set forth in claim 12 wherein a nonmetallic antistatic film is formed on the phase-shifter film formed on said substrate through a resist film for electron beam-exposure.
 21. The phase-shifting photomask blank as set forth in claim 13 wherein a nonmetallic antistatic film is formed on the phase-shifter film formed on said substrate through a resist film for electron beam-exposure.
 22. A phase-shifting photomask characterized in that a part of a light-translucent film of the phase-shifting photomask blank as set forth in claim 11 is removed through a patterning treatment to form a pattern which consists of the resulting light-translucent portions and light-transmitting portions capable of transmitting light rays having an intensity which can substantially contribute to exposure.
 23. A device for manufacturing a phase-shifting photomask blank in which a thin film is formed by supplying a reactive gas to a film-forming chamber and depositing said thin film on a substrate using a reactive sputtering technique, while passing said substrate over a target, wherein it is designed to have an opening whose length is sufficiently enlarged along a substrate-conveying direction so that even regions whose deposition rate of a target component is not more than 90% of a maximum level thereof also contribute to the film-formation. 